产品规格书/Specification高温烧结银浆 陶瓷烧结银浆 高温导电银浆
产品/product: | 大功率电阻浆料/ High-power Resist paste |
料号/Part number: | 05H06 series |
适用范围/Application:
此产品适用于大功率电阻使用。
The resistor paste applies to High power Resistor.
使用条件/Operating conditions:
基材 Substrate | 氧化铝陶瓷 96% alumina、surface roughness 3-5μm |
印刷 Printing | 200-250目丝网印刷 200-250 mesh stainless screen |
流平 Levelling | 室温下流平5-15分钟(时间根据流平的实际情况决定)。 5-15min minutes at room temperature |
干燥 Drying | 通风烘箱烘烤100-150℃,10-15分钟 (空考温度低于300℃,可根据烘烤的实际情况决定烘烤时间。) 100-150℃10-15 min |
烧结 Firing Condition | 隧道炉空气气氛下烧结,峰值850±2℃(推荐值),9-11分钟。 Atmospheric firing in belt furnace with peak time of 9-11 Minutes at 850±2℃ |
Thinner | ST1000,ST1001 |
性能/Characteristics:
1.浆料性能/Paste Characteristics:
性能Characteristic | 标准Standard | 测试方法及条件 Test method and conditions | |
1 | Fineness | ≤8μm | FOG test |
2 | Viscosity | 100-200Pa.s | Brookfield HBT utility cup and spindle (SC4-14/6R), 10rpm,25±1℃, Brookfield HBT(博利飞)粘度计,转子SC4-14/6R), 10rpm,25±1℃ 粘度可根据用户实际需要调节。 |
2.烧结后特性/Characteristics after firing:
在1烧结条件下,膜厚8-12mm Check fired film produced under the conditions specified in 1), (Film thickness is 8-12mm.)
特性 Characteristics | Standard 标准 | 测试方法和条件 Test method and conditions | |
3 | 外观 Appearance | 紧凑,致密 Compact and unknit | Eyeballing |
4 | 方阻值 Resistivity |